Well cementing method using a composition having improved flow properties, containing sulfonated copolymers of styrene-maleic anhydride

ABSTRACT

Aqueous hydraulic cement compositions containing sulfonated copolymers of styrene-maleic anhydride as flow-property-improving and turbulence-inducing additives and their use in cementing wells is disclosed.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to an aqueous hydraulic cement slurry composition especially suitable for use in cementing a well.

More particularly, the present invention concerns sulfonated copolymers of styrene-maleic anhydride as additives for hydraulic cements used in cementing gas and oil wells which improve the flow properties of the cement slurry, especially facilitating high flow rates and turbulent flow of the cement slurry when it is being pumped to its desired location during the cementing operation.

As used herein, the terms "improve the flow properties" or "flow-property-improving" are intended to describe the manner in which the sulfonated copolymers of styrene-maleic anhydride of the present invention facilitate or render more efficient the pumping of cement slurries, particularly the pumping of well cement slurries during primary cementing operations. This action is apparently due primarily to a reduction in the frictional drag experienced by the cement slurry while it is being pumped or moved through a confining passageway, but it is not intended to limit the described action to such a friction reducing effect, since other effects may also play a role.

The term "turbulence-inducing" is intended to describe the effect of the sulfonated copolymers of styrene-maleic anhydride of the present invention in promoting the departure of a moving cement slurry from laminar flow to turbulent flow. The slurry in such a state of flow no longer moves in laminae aligned along the confining conduit, but experiences a disorganized flow characterized by eddies and disturbances. The flow-property-improving and turbulence-inducing additives of the present invention reduce the apparent viscosity of a cement slurry, which in turn reduces the flow rate required to cause turbulent flow. Thus, the promotion of turbulent flow may take place simply as a reduction in the amount of pumping pressure or volume necessary to induce a state of turbulent flow for a particular cement slurry under specific pumping conditions, below that which would be required if the turbulence-inducing additive were omitted from the cement slurry composition.

Techniques for drilling and completing wells, particularly gas and oil wells, are well-established. Of chief concern here are those wells which are drilled from the surface of the earth to some subterranean formation containing a fluid mineral which it is desired to recover. After the fluid-containing geologic formation is located by investigation, a bore-hole is drilled through the overlying layers of the earth's crust to the fluid-containing geologic formation in order to permit recovery of the fluid mineral contained therein. A casing is then secured in position within the bore-hole to insure permanence of the bore-hole and to prevent entry into the well of a fluid from a formation other than the formation which is being tapped. This well casing is usually cemented in place by pumping a cement slurry downwardly through the well bore-hole, which is usually accomplished by means of conducting tubing within the well casing. The cement slurry flows out of the open lower end of the casing at the well bottom and then upwardly around the casing in the annular space between the outer wall of the casing and the wall of the well bore-hole. The drilling process which produces the bore-hole will usually leave behind on the wall of the bore-hole produced, a drilling fluid filter cake of mud-like material. This material is a barrier to the formation of proper bonding by any cement composition employed to produce an impermeable bond between the casing and the well wall. As a result, cementing operations have often proven inadequate, permitting fluids from other formations to migrate into the producing formation, and vice versa. Prior art solutions to this problem have included washing away the filter cake from the well wall prior to the cementing operation. However, the washing liquids themselves have introduced new problems, including reduced permeability of the producing formation.

Nevertheless, an effective cementing operation requires that the drilling fluid filter cake be removed from the well bore wall and replaced by the cement slurry in order to permit the formation of a solid layer of hardened and cured cement between the casing and the geologic formations through which the well bore-hole passes. It has been recognized in the art that removal of the drilling fluid filter cake may be accomplished by a sufficiently high flow rate for the cement slurry during its injection into the well bore-hole. Such a high flow rate will usually occur as turbulent flow.

The flow properties of cement slurries are also important during primary cementing operations in other respects. The pressure drop in the annulus beng cemented which results from friction will increase both the hydraulic horsepower required to move the cement slurry into place in a given time period, as well as the hydrostatic pressure exerted on the producing formation. Moreover, some investigators have felt that obtaining actual turbulent flow of the cement slurry is not necessary to remove the drilling fluid filter cake, and that high flow rates are sufficient where the drilling fluid has low gel strength and there is good centralization (concentric placement of the well casing within the well bore-hole). Consequently, the present invention is directed to well cementing compositions having improved flow properties, including, but not limited to, adaptability to turbulent, especially high turbulent flow.

Prior to the discovery of flow-property-improving, especially turbulence-inducing additives for well cement compositions, achieving high flow rate and turbulent flow for conventional cement slurries presented a number of problems not normally encountered with less viscous fluids. Inducing turbulence by control of flow rate alone has required a certain minimum velocity, which in turn is dependent upon maintaining a certain minimum pressure. Particularly, where the turbulence induced is sufficient to assure removal of the drilling fluid filter cake, additional pumping capacity and very high pressure levels are required. Producing high flow rates has, of course, required the same measures. These required pressure levels, especially for deep wells, have often exceeded the pressure at which many subterranean formations break down, thus giving rise to a problem of lost circulation. It also may happen that the required pressure level exceeds the capacity of the pumping equipment or the endurance of the well drilling and associated apparatus.

The present invention facilitates pumping of cement slurries at high flow rates and permits pumping of cement slurries in turbulent flow at significantly lower flow rates than would be possible using conventional cement slurry compositions, by adding to the said cement slurries a flow-property-improving and turbulence-inducing agent. The lower flow rates required for turbulence result in a corresponding reduction in the pump pressures required to force the cement slurry into place in the desired manner. Correspondingly, higher flow rates may be achieved with a reduced amount of required pressure and pumping capacity.

The present invention also permits increased use of fluid-loss control agents which have a viscosity-increasing effect on cement slurries with which they are employed. This thickening tendency otherwise requires use of only small amounts of fluid-loss control agents to avoid problems in pumping of an overly viscous cement slurry. Use of the flow-property-improving and turbulence-inducing additives of the present invention in conjunction with fluid-loss control agents produces a cement slurry having desirable flow properties, yet containing adequate quantities of the fluid-loss control agent.

2. Description of the Prior Art

U.S. Pat. No. 3,359,225 discloses an additive for Portland-type cements comprising polyvinylpyrrolidone and the sodium salt of naphthalene sulfonate condensed with formaldehyde. The additive reduces the friction encountered as the cement is flowed or pumped into place, and also permits the utilization of decreased quantities of water in the cement mixture. Kucera -- U.S. Pat. No. 3,465,824 discloses an aqueous hydraulic cement slurry containing a bisulfite-modified phenol-formaldehyde condensation product which serves as a turbulence inducer to the slurry while being moved in a confined passageway. Hook et al. -- U.S. Pat. No. 3,465,825 discloses an aqueous cement slurry containing a turbulence inducing agent comprising the lithium salt of the condensation product of mononaphthalene sulfonic acid and formaldehyde. Scott et al. -- U.S. Pat. No. 3,511,314 discloses an aqueous hydraulic cement slurry containing a turbulence-inducing, fluid-loss control agent consisting of the reaction product of (1) an amino compound selected from the group consisting of polyalkylenepolyamines, polyalkylenimines, and their mixtures, and (2) an acidic compound selected from the group consisting of carboxylic acids, sulfonic acids, polymers having a carboxyl substituent, and polymers having a sulfonate substituent. Messenger -- U.S. Pat. No. 3,558,335 discloses cement compositions comprising hydraulic cement in admixture with a turbulence inducer and silica or diatomaceous earth particles. A number of known turbulence inducers are set out, particularly sodium dodecylbenzenesulfonate and sodium polystyrenesulfonate. Dietz et al. -- U.S. Pat. No. 2,905,565 discloses cement slurries possessing good flow properties containing salts of polyvinyl sulfonic acid, aromatic compounds containing a plurality of sulfonic or carboxylic acid groups, and copolymers prepared from components such as maleic acid and vinyl sulfonic acid, among other compositions. Shen et al. -- U.S. Pat. No. 3,268,563 discloses compositions useful as cement additives for improving strength and hardening time, comprising poly(α-sulfo carboxylic acids), with maleic acid being disclosed in particular. Harrison -- U.S. Pat. No. 3,409,080 discloses polymeric fluid-loss agents for cementing compositions, included among which are copolymers of maleic anhydride and polystyrenesulfonate.

SUMMARY OF THE INVENTION

In accordance with the present invention there is provided a well cementing composition comprising hydraulic cement, water, and from about 0.01 to about 5.0% by weight of the cement of a flow-property-improving and turbulence-inducing additive comprising sulfonated copolymers of styrene-maleic anhydride. Preferably, this composition contains from about 0.1 to about 2.0% by weight (based on dry weight of cement) of the additive. The present invention also provides a method of cementing which employs the cement composition just described.

The sulfonated copolymers of styrene-maleic anhydride employed as flow-property-improving and turbulence-inducing additives for well cementing compositions in the present invention are water soluble and the said additives comprise copolymers of randomly repeating units of the following formulas: ##EQU1##

where M is hydrogen, ammonium or alkali metal ion, and n is an integer of 1 to 3.

The styrene may be sulfonated to the extent of 2 or even 3 sulfonic acid or sulfonate groups per sytrene unit. However the extent of sulfonation will ordinarily be slightly in excess of 1.

It will be appreciated that the maleic anhydride may become hydrolyzed to form maleic acid. Maleic acid or salts thereof may also be employed initially. The term "maleic anhydride" as employed herein is intended to include the maleic acid and maleic acid salts as well as the anhydride.

The ratio of sulfonated styrene to maleic anhydride in the copolymer may vary considerably, from 100:1 to 1:100. However, it has been found that a ratio of the components of approximately 2:1 to 1:2, and particularly of about 1:1, is not only practical but gives satisfactory results as well.

The molecular weight of the copolymer may be as high as 100,000 or more. Preferred, however, are copolymers of lower molecular weight, in the range of 3,000-10,000.

The sulfonated copolymers of styrene-maleic anhydride of the present invention may be prepared according to any of a number of conventional methods for their preparation. Any such polymerization method giving copolymers of the type described above, in satisfactory yields of acceptably pure product, will prove satisfactory.

The compositions and methods of the present invention may employ any type of hydraulic cement. Hydraulic cement is defined as any cement which will set or cure under the action of water, and is intended to include all mixtures of lime, silica and alumina, or of lime and magnesia, silica, and alumina and iron oxide. Hydraulic cements include hydraulic limes, grappier cements, pozzolan cements, natural cements, and portland cements. Pozzolan cements include slag cements made from slaked lime and granulated blast furnace slag. Among these hydraulic cements, the portland cements are preferred, chiefly because of their superior strength characteristics. The term portland cement is intended to include any cement regarded in the cementing art as a portland cement, usually as defined by standard reference works. The precise composition of any one particular portland cement will vary from another, but generally portland cements are produced by mixing and grinding together a calcareous and an argillaceous material, kiln heating the mixture (1350° to 1800°C.) until vitrification begins, pulverizing the clinker thus produced and mixing the same with a small amount of gypsum. The portland cements may be ground to any desired particle size, and grading of portland cements is on the basis of the specific surface of the cement, which will range between 1200 and 2600 square centimeters per gram. Grading is also based on the amount of cement particles retained on a No. 325 Screen, U.S. Sieve Series. Thus, preferred oil well cements have a specific surface of about 1480 square centimeters per gram and about 85% by weight passes through a No. 325 Screen.

The hydraulic cement may be employed alone in preparing the cementing composition of the present invention, merely being admixed with water and the flow-property-improving and turbulence-inducing additive, or it may have additionally incorporated there any of a number of conventional cement additives. For example, the cement may include a minor portion, up to about 2.0% by weight of dry cement, of a retarder composition. Such an additive is preferred for oil well cements, since cementing operations are conducted under ambient well bottom temperatures which can exceed about 200°F. Examples of conventional retarder compositions include carboxymethylhydroxyethylcellulose, borax, dehydrated borax, calcium lignosulfonate and ferrochrome lignosulfonate.

Fluid-loss control agents may be employed, as previously discussed. Well-known fluid-loss agents include such materials as polyvinylpyrrolidone, polyvinyl alcohol, polyvinylacetate and carboxymethylhydroxyethyl cellulose.

Weighting components comprising inert materials such as barite and ilmenite are often employed. Silica may be employed to retard high temperature strength retrogression.

Other known additives conventionally employed with cementing compositions may be employed with the cementing compositions of this invention, and in amounts sufficient to produce the intended modification of the cementing composition characteristics for which any additive was selected. More than one such additive, may, of course, be employed at the same time.

The dry hydraulic cement component of the cementing composition of the present invention is admixed with water to form a pumpable, settable cement slurry. The water which is employed to form this cement slurry may be any naturally occuring water suitable for preparing cement slurries. Particularly, brines of any concentration of calcium chloride or sodium chloride or their mixtures are suitable. Sea water may be employed and is thus convenient in off-shore operations. The water should be employed in an amount which is sufficient to produce a pumpable, settable slurry. Excessive amounts of water may produce a weakened finally set cement which is lacking in homogeneity owing to the settling of the aggregate portions thereof. Proper amounts of water for producing a suitable cement slurry are described in technical publications, such as the bulletins of the American Petroleum Institute (API). Increasing water content in a cement composition effects a lowering of the plastic viscosity of the cement slurry, which results in the slurry being more readily pumped in turbulent flow. However, the water content should not be in excess of the amount which will give 4.0 ml. of supernatant water for a 250 ml. sample of cement slurry which has been allowed to stand undisturbed in a 250 ml. graduated cylinder for a period of two hours. The type of hydraulic cement composition employed will also, of course, determine the amount of water required. Other factors are significant as well. For example, where silica is added to the cement composition, and high temperatures are encountered in the cementing operation (above about 250°F.), additional amounts of water will be required. Generally, the amount of water necessary to give a settable cement composition having the required characteristics, which contains the flow-property-improving and turbulence-inducing additive of the present invention, will be in an amount of from about 25% to about 60% by weight, based on the weight of dry hydraulic cement.

Water content may be varied in order to effect a change in the density of the cement slurry. It is customary practice to employ a cement slurry which has a density at least as great as that of the drilling fluid used in the drilling operation. Thus densified slurries may be produced by diminishing the amount of water which would otherwise be employed.

The procedure for preparing the cementing compositions of the present invention does not require any particular sequence of steps. The flow-property-improving and turbulence-inducing additives of the present invention may be simply added to the water which is used to produce the final cement slurry composition. When other conventional additives are employed, they may be incorporated into the final cement slurry composition in any known suitable manner.

The influence of the turbulence-inducing additives of the present invention on the rheological properties of the total cement slurry composition is susceptible to mathematical characterization. Expert opinion varies as to the correct theoretical model, and thus the proper mathematical characterization of the rheological properties of cement slurries. They have been treated according to the principles of Bingham plastic fluids as well as according to the Power Law concept. The mathematical formulation is based on Fann Viscometer readings, as will be described hereinafter.

The behavior of cement slurries may be viewed as governed by the Power Law concept. For a mathematical characterization of this concept, two slurry parameters are determined: the flow behavior index (n') and the consistency index (K'). A Fann Viscometer may be used to make these determinations. The instrument readings at 600 and 300 r.p.m. are recorded and the values for n' and K' are then calculated as follows: ##EQU2##

where N is the extension factor of the torque spring of the particular Fann Viscometer instrument.

Turbulence is promoted when the flow behavior index (n') value is higher than that of an untreated slurry.

The so-called Reynolds Number for a fluid moving through a conduit is the critical value at which the flowing fluid will begin to flow in turbulence. The Reynolds Number may be calculated according to the following equation: ##EQU3## where: N_(Re) is the Reynolds Number (dimensionless),

V is the velocity, feet per second,

ρ is the slurry density, pounds per gallon,

n' is the flow behavior index (dimensionless),

K' is the consistency index, pound-seconds per square foot,

D is the inside diameter of the pipe, inches.

The velocity (V_(c)) at which turbulence may begin is readily calculated from the following equation, which is derived from the equation for the Reynolds Number, and assumes a Reynolds Number of 2100: ##EQU4##

where the different elements of the equation have the same meaning as indicated above for the Reynolds Number equation. Where the conduit through which the cement slurry passes is the annulus between the well casing and the well wall, D = D_(O) - D_(I), where D_(O) is the outer inside diameter or hole size in inches, and D_(I) is the inner pipe outside diameter in inches.

The Power Law concept equation will give higher flow rates, or lower flow rates required to produce turbulence where the Fann Viscometer readings are reduced.

EXAMPLE 1 Fann Viscometer Readings for Cementing Compositions Containing Sulfonated Copolymers of Stryene-Maleic Anhydride

A 38% Class H (API Class H cement has a fineness in the range of 1400-1600 sq. cm./gram and contains, in addition to free lime and alkali, the following compounds in the indicated proportions: tricalcium silicate -- 52, dicalcium silicate -- 25, tricalcium aluminate -- 5, tetracalcium aluminoferrite -- 12, and calcium sulfate -- 3.3.) cement slurry was made up by adding tap water (228 ml.) to a Waring blender, dissolving the indicated amount of sulfonated copolymer of styrene-maleic anhydride, turbulence-inducing additive in the water, then mixing in the cement (600 g.) at low speed. The resultant slurry was then mixed at high speed for 35 seconds. The slurry was then stirred in a Halliburton consistometer for 20 minutes at room temperature. The viscosity of the slurry was then immediately measured on a Fann Viscometer equipped with a No. 1 spring. The instrument readings for various speeds were recorded and are illustrated in the table of values below.

    __________________________________________________________________________              % Additive                                                                            Fann Viscosities at                                                                             Flow                                          Turbulence-                                                                             (based on                                                                             Indicated R.P.M's                                                                               Behavior                                      Inducing weight of               Index                                         Additive dry cement)                                                                           600  300                                                                               200 100  (n')                                          __________________________________________________________________________     Control* --     145 87.5                                                                               77.5                                                                               53.5 0.73                                          Sulfonated                                                                              1.0     57 19  11.5                                                                               7.5  1.58                                          Copolymer of                                                                   Styrene-Maleic                                                                          0.5     55 22.5                                                                               14.5                                                                               6.5  1.29                                          Anhydride                                                                               0.3    103 55.5                                                                               41  27   0.89                                          __________________________________________________________________________      *Neat Class H cement.                                                    

EXAMPLE 2 Fann Viscometer Readings for Brine Cementing Compositions Containing Sulfonated Copolymers of Styrene-Maleic Anhydride

The procedures of Example 1 above were repeated, except that instead of tap water, 10% NaCl and 5% KCl (both percentages by weight) aqueous solutions were employed, thus giving simulated brine-prepared cement slurries. The samples were tested at 100°F. and 190°F., thus simulating higher temperatures encountered in deeper well bottoms. The Fann Viscometer readings and calculated flow behavior index (n') values are illustrated in the table of values below.

    __________________________________________________________________________     A. At 100°F.:                                                           1. Cement Slurry with 10% NaCl:                                                         % Additive                                                                            Fann Viscosities at     Flow                                   Turbulence-                                                                             (based on                                                                             Indicated R.P.M.'s      Behavior                               Inducing weight of                      Index                                  Additive dry cement)                                                                           600   300   200   100   (n')                                   __________________________________________________________________________     Control* --     195   141   123   102   0.46                                   Sulfonated                                                                     Copolymer of                                                                            0.5    75    41    31    19    0.87                                   Styrene-Maleic                                                                 Anhydride                                                                      __________________________________________________________________________     2. Cement Slurry with 5% KCl:                                                  Control* --     126.5 87    74    61.5  0.54                                   Sulfonated                                                                     Copolymer of                                                                            0.5    96    62    51.5  39    0.63                                   Styrene-Maleic                                                                 Anhydride                                                                      __________________________________________________________________________     B. At 190°F.:                                                            Cement Slurry with 5% KCl:                                                             % Additive                                                                            Fann Viscosities at     Flow                                   Turbulence-                                                                             (based on                                                                             Indicated R.P.M.'s      Behavior                               Inducing weight of                      Index                                  Additive dry cement)                                                                           600   300   200   100   (n')                                   __________________________________________________________________________     Control* --     177   140   147   84    0.33                                   Sulfonated                                                                     Copolymer of                                                                            0.5    130   63    38    22    1.04                                   Styrene-Maleic                                                                 Anhydride                                                                      __________________________________________________________________________      *Neat Class H cement.                                                    

The flow-property-improving and turbulence-inducing additives of the present invention are employed to prepare cementing compositions which are readily pumped in turbulent flow during a cementing operation at a satisfactorily low pump rate. The additives are also used to advantage simply to reduce the pumping pressure required for a given flow rate, or to obtain a higher flow rate at a given pumping pressure. The cementing composition of this invention which has improved flow properties and is easily flowed in turbulence is employed in the conventional cementing operation in the same manner as would a cementing composition which did not contain the flow-property-improving and turbulence-inducing additive, but which was otherwise the same composition.

Obviously, many modifications and variations of the invention as hereinabove set forth can be made without departing from the essence and scope thereof, and only such limitations should be applied as are indicated in the appended claims. 

What we claim is:
 1. In the method of cementing a well comprising the step of pumping an aqueous hydraulic cement slurry into place in the annular space between the well casing and the well bore-hole, the improvement comprising employing therein an aqueous hydraulic cement slurry composition having improved flow properties comprising dry hydraulic cement in admixture with from about 0.01 to about 5.0 percent by weight, based on weight of dry hydraulic cement, of a copolymer of randomly repeating units of the following formulas: ##EQU5## where M is hydrogen, ammonium or alkali metal ion, and n is an integer of 1 to 3; andsufficient water to make a pumpable slurry which is capable of setting to form a monolithic solid.
 2. The method of claim 1 wherein the copolymer has a molecular weight of from 3,000 to 10,000.
 3. The method of claim 1 wherein for the said cement slurry composition employed therein, the copolymer is admixed with the hydraulic cement in an amount of from about 0.1 to about 2.0 percent by weight, based on weight of dry hydraulic cement.
 4. The method of claim 1 wherein for the said cement slurry composition employed therein, the water is present in an amount of from about 25 to about 60 percent by weight, based on weight of dry hydraulic cement.
 5. In the method of cementing a well, comprising the step of pumping into place in the annular space between the well casing and the well bore-hole an aqueous hydraulic cement slurry which is flowing in turbulence for the purpose of removing any drilling fluid filter cake accumulated on the well bore-hole surface, the improvement comprising employing therein an aqueous hydraulic cement slurry composition being more readily induced to flow in turbulence, comprising dry hydraulic cement in admixture with from about 0.01 to about 5.0 percent by weight, based on weight of dry hydraulic cement, of a copolymer of randomly repeating units of the following formulas: ##EQU6## where M is hydrogen, ammonium or alkali metal ion, and n is an integer of 1 to 3; andsufficient water to make a pumpable slurry which is capable of setting to form a monolithic solid.
 6. The method of claim 5 wherein the copolymer has a molecular weight of from 3,000 to 10,000.
 7. The method of claim 5 wherein for the said cement slurry composition employed therein, the copolymer is admixed with the hydraulic cement in an amount of from about 0.1 to about 2.0 percent by weight, based on weight of dry hydraulic cement.
 8. The method of claim 5 wherein for the said cement slurry composition employed therein, the water is present in an amount of from about 25 to about 60 percent by weight, based on weight of dry hydraulic cement. 